Въведение: Какво е Твърдост

Твърдост е собственост на всеки материал да устои деформации на формата си, когато е подложен на външна сила. Твърдост тестване е важно за технически и инженерни приложения, тъй като помага да се определи твърдостта и якостта на опън на материали.

It helps to develop a clear understanding of whether the specimen being tested is suitable for specific applications. It helps industries to make safe and high-quality end products which meet the safety regulations and guidelines laid down by the relevant authorities.

The different types of hardness and various methods of hardness testing and determining the hardness values are discussed below:

Scratch Твърдост

Scratch hardness is the ability of a material to resist deformation usually by scratches and abrasions. Scratch hardness is one type of hardness which is measured when a specimen surface is scratched by a stylus which is dragged along its surface under a fixed test load.

Scratch hardness method defines the resistance of a material to plowing by a hard stylus. It measures the hardness of the material and its ability to resist scratches and abrasions. Generally, a scratch hardness tester consists of a stylus, portable sample holding stage, load-applying device, and a data processing and display unit.

Многофункционален тестер за твърдост

Buy PHE-5000/150 Microcomputer Control Electron Universal Testing Machines (Two in 0ne Machine)

$ 100,00
$ 1,470.00

Твърдост по Бринел тестер

On Sale HB-2 Hammering Brinell Hardness Tester 100-450HBS

$ 118.00

Твърдост по Бринел тестер

Buy Multi purpose Electric Surface Rockwell & Vickers Hardness Tester

$ 2,000.00
$ 4,411.00

Твърдост по Бринел тестер

Free Shipping Electronic Brinell Hardness Tester 8~650 HBW

$ 1,911.00

The earliest scratch hardness tests were conducted by Friedrich Mohs in 1820 who also developed the Mohs scale. The scratch hardness test measures the resistance of the specimen to fracture or permanent deformation due to friction caused by the stylus along its surface.

This test uses a harder material to scratch the specimen surface which is made of a relatively softer material. When you need to test coatings, then scratch hardness refers to the force which is necessary to cut through the film to the substrate. Mohs scale is used for measuring the scratch resistance of material along with a measuring device known as sclerometer.

отстъп Твърдост

Indentation hardness refers to the hardness of a material which is determined by making an indentation on its surface using an appropriate indenter under a test load.

READ  How is hardness measurement more convenient than a tensile test?

Има много различни методи вдлъбнатина за изпитване, които измерват дълбочината на вдлъбнатина, изработен върху повърхността на образец за измерване на твърдостта му. Идентификационния тест твърдост могат да бъдат допълнително разделени на две категории-макро тестове идентификационния и микро-идентификационния тест. Макро тестове отстъп да се възползват от големи натоварвания, по-голяма от 1Kgf и могат да отидат до 3000Kgf в някои случаи.Автоматично оръдейна Digital Display ниско натоварване твърдост по Викерс тестер

Известният тип макро методи вдлъбнатина изпитване включва метод Rockwell твърдост тестване, метод Бринел, тест Викерс, Knoop метод твърдост тестване и т.н. тестване Микро-вдлъбнатина, от друга страна, се използва за измерване на твърдостта на меки метали, тънки и малки образец, и т.н.

тестовите натоварвания, прилагани за тестове микро-идентификационния твърдост са много по-ниски и могат да варират между 1 до 1000gf. тестове Микро-идентификационния могат да бъдат използвани за измерване на промените в твърдост на микроскопичен мащаб. метод Викерс и методи за изпитване на твърдост Knoop два популярните методи за изпитване на твърдост микро-идентификационния.

Идентификационния тест за твърдост може да бъде оставен грешки. Основните източници на грешки при измерване на твърдост включват лоша техника, неправилно калибриране на оборудването, тестване, неправилното завършване на повърхността на образеца, и т.н. Изпитвателната повърхност трябва да бъде свободен от всякакви замърсявания, окисление, или смазване, за да получите надеждни оценки на твърдост. В Indenter трябва да бъде перпендикулярна на повърхността на образеца като всеки наклон ще доведе до погрешни измервания твърдост.

Rebound Твърдост

Rebound hardness which is also known as dynamic hardness measures the hardness of a material by determining the height to which a diamond-tipped hammer bounces when it is dropped from a height on to the specimen. This type of hardness is related to elasticity.

Rebound hardness is generally measured using the Leeb rebound hardness test. This method was developed in 1975 by Leeb and Brandestini by using a portable hardness tester. This tester provided a new alternative to the usually intricate and complex traditional hardness testing equipment.Автоматично оръдейна Програмиран Digital Display твърдост по Викерс тестер

The Leeb rebound hardness testing method follows standardized procedures. The velocity of the body ranges between 1.4 m/s to 3 m/s. Under this method, the velocity of the body before and after the impact is measured to determine the hardness of the specimen.

The ratio of the impact velocity to the rebound velocity gives the dynamic Leeb hardness of the test specimen. The object used for making the impact on the specimen can be tungsten carbide cobalt, ceramic or diamond, or a ball-shaped indenter with different radius.

The sample hardness determined by this method is represented as (example) 750 HL D in which 750 denotes the hardness value, HL denotes “Hardness according to Leeb” and D represents Leeb method with spherical impact body of tungsten carbide-cobalt with a radius of 1.5 mm and weight of 4.5 grams.

Избирането Твърдост метод за тестване на най-добрите

The hardness of a material depends on a number of factors like homogeneity of the material, type of material, its size, and condition.

There are different types of methods for hardness testing which needs to be selected carefully for getting the most accurate and reliable hardness measurements.

Компютърна микротвърдост тестер (полуавтоматична) за Програмиран Carrier Таблица
Компютърна микротвърдост тестер (полуавтоматична) за Програмиран Carrier Таблица

Factors which need to be considered before selecting the ideal hardness testing methods include- the type of material to be tested, the hardness of the material to be tested, homogeneity of the material, size of the specimen, if mounting is necessary for hardness testing, thickness of the specimen, etc.

READ  Difference between Rockwell, Vickers and Brinell Tests

Rockwell тест на твърдостта

Rockwell hardness testing is the most common and fast method for testing hardness. It is generally ideal for testing hardness of larges sized samples.

It can be used either on the assembly line or in laboratories for testing hardness. It uses a steel ball or diamond-tipped cone indenter for measuring hardness depending upon the hardness of the material to be tested.

To start the Rockwell test, a minor load of generally 10Kgf is applied on the indenter. The indenter then moves under the test load on to the specimen surface. While the indenter is still under the influence of the minor test load, an additional major test load is also applied to it. This ensures better indentation on the specimen surface which is clear and measurable.

The Rockwell method of hardness testing is popular as it is not influenced by either the operator’s bias or the roughness of the surface whose hardness is being tested.

It does not make use of any sophisticated or costly optical equipment for measuring the hardness of specimen, which makes it a cost-effective method for hardness testing. It is a non-destructive method for hardness testing which means that the sample specimen being tested is not destroyed and it can be used for other purposes after the testing procedure is completed.Rockwell Твърдост тестер (класически тип)

This method has its drawbacks also as it is not very accurate compared to other methods of hardness testing. Small deviation in measuring the indentation depth can throw off the hardness readings considerably.

If the indenter in this method is worn out, then it can provide faulty hardness measurements which are non-reliable.

Rockwell стойност твърдост се изчислява графики курсове. Има близо 30 Рокуел везни, но повечето от материалите са обхванати от Rockwell С и В мащаби. Стойностите на твърдост по Rockwell изпитване са представени като (например) 70 HRB където 60 е твърдост четене по скалата на B.

 

Твърдост по Бринел Test

Изпитването на твърдост по Бринел е един от най-старите и най-широко използваните методи за изпитване на твърдост материали. Този метод е разработен от Джуниър Ачийвмънт Бринел в годината 1900. Той е идеален за измерване на твърдостта на екземпляри, които са прекалено груба или курс, за да се измери чрез други методи.

Методът на Бринел включва използването на по-голямо натоварване на изпитвания, които може да стигнат до 3000Kgf и топка Indenter общо 10 mm в диаметър.Електрически Surface Рокуел Твърдост тестер

For measuring the hardness of softer metals and alloys, smaller test loads of up to 500Kgf are also used. The predetermined test load is applied to the spherical indenter which is held to the specimen surface for generally for 10-15 seconds and then moved.

The indentation depth made by the indenter on the specimen surface is then measured and studied using advanced optical equipment which ensures better accuracy and reliability.

The Brinell conversion chart is then used to convert the average diameter of the indentation made to the corresponding Brinell hardness value. Using the conversion charts, the Brinell hardness value can also be converted into the corresponding tensile strength.

The Brinell method of hardness testing comes with few drawbacks also. The operator can make mistakes in measuring the indentation depth on the specimen surface which can considerably impact the hardness measurements.

READ  How to test the hardness of metals?

Since the method involves advanced and sophisticated optical equipment for measuring the specimen hardness, it is costlier compared to the Rockwell method. It also takes more time to test hardness as the specimen surface needs to be prepared before testing.

The Brinell method will also not work accurately if the specimen surface is too thin i.e. less than 9.6 mm.

стойности на твърдостта по Бринел използване на метода са представени като 600 HBW където 600 означава стойността на твърдост и HBW означава "твърдост по Бринел" с волфрамов топка Indenter. Ако стоманено топче Indenter се използва след това показанията ще бъдат представени като 600 HBS където HBS обозначава "твърдост по Бринел" със стоманена топка Indenter.

Твърдост по Викерс Test

тест Vickers използва същия принцип като метода на Бринел с изключение единствено на вида на Indenter се използва.

Видът на Indenter трябва да се промени по метода на Бринел в зависимост от вида на материала, което се изпитва. Въпреки това, същата диамант Indenter се използва в метода на Викерс за измерване на твърдостта на всички образци видове.Автоматично оръдейна Digital Display ниско натоварване твърдост по Викерс тестер

The indenter used in this method is in the form of a right pyramid. A test load is applied on the indenter which presses itself against the specimen surface thereby leaving an indentation.

The diagonal lengths of these indentation marks are measured using optical systems, resulting in highly accurate hardness readings. The dwell time- the time for which the test force is applied through the indenter on the specimen surface- is generally between 10-15 seconds in this method.

The Vickers test using micro-test loads which are much lesser compared to the Brinell method. It is a microhardness testing method which is best suited for measuring the hardness of materials which are too thin or small for macro hardness testing.

Този метод е най-подходящ за измерване на твърдостта на тънки листове от метали, малки образци и др тест Викерс е безразрушителен метод, който гарантира, че пробата могат да бъдат използвани след тестването е завършена. Има няколко ограничения на метода на Викерс.

Тя изисква повърхността на образеца, за да бъдат свободни от всякакви несъвършенства и по този начин е необходимо време за подготовка повърхността на образеца преди провеждане на теста. Това отнема най-малко 30-60 секунди за извършването на това изследване и времето е изключително на времето, необходимо за подготовка на повърхността на образеца.

Vickers тестване не се препоръчва за насипни производство в поточни линии и е по-подходящ за лабораторни изследвания. Измерването на твърдостта в теста Викерс са представени като 700 HV / 10, където 700 е твърдост по Викерс стойност, която е била получава чрез използване на тест сила 10Kgf.

Кнооп тест на твърдостта

Knoop hardness testing method is an alternative to the Vickers method. It is a microhardness measuring method which is suitable for measuring the hardness of fragile and brittle materials like ceramics. It is also useful for hardness testing of small elongated areas like coatings.

The Knoop method also uses a pyramidal diamond as indenter, but the indenter is elongated instead of being a right pyramid as in the Vickers method. Since the method is used for hardness testing of fragile materials, it uses micro loads of up to 1Kgf.

The indenter used in this method penetrates the specimen surface only half as deep as in the Vickers method, which makes it perfect for hardness testing of the brittle specimen.

Поради формата на Indenter, методът на Кнооп е по-подходящ за измерване на вече удължени екземпляри като покрития. Важно е да се отбележи, че повърхността на образеца трябва да бъдат подготвени правилно преди провеждане на теста Кнооп за осигуряване на точни и надеждни измервания на твърдост.

 

Оставете коментар

Your email address will not be published. Required fields are marked *

Chat with us
Chat with us
Leave a Message & We will reply within 12 Hours!
Connecting...
Leave a Message & We will reply within 12 Hours!
Leave a Message & We will reply within 12 Hours!
:
:
:
Leave a Message & We will reply within 12 Hours!
:
:
This chat session has ended
Was this conversation useful? Vote this chat session.
Good Bad